1.danci.911cha.com1.目的评价金沉积、金合金和镍铬合金3种不同基底烤瓷冠临床应用效果。ObjectiveTocomparetheclinicaleffectofthecera

1. danci.911cha.com

1. 目的评价金沉积、金合金和镍铬合金3种不同基底烤瓷冠临床应用效果。
Objective To compare the clinical effect of the ceramic crowns made of Ni-Cr alloy, gold alloy, gold-electroforming.

2. 镍铬烤瓷的意思

2. 目的在体外模拟环境下,研究溶胶凝胶法制备的涂层对牙科烤瓷镍铬合金耐腐蚀性能的影响。
Objective To investigate the effects of Sol-Gel coating on the corrosion resistance of nickel-chronium alloys in vitro.

3. 镍铬合金试件、烤瓷试件、新鲜离体上中切牙、烤瓷熔附金属全冠共60例,分6组,每组10例。1组:Ni-Cr合金+Clearfil SE BOND+复合树脂;2组:烤瓷+Clearfi SE BOND+复合树脂;3组:Ni-Cr合金+Lute+复合树脂;4组:烤瓷+Lute+复合树脂;5组:牙釉质+Durafill Bond+复合树脂;6组:烤瓷熔附Ni-Cr合金。1~5组修复材料均为Durafill vs口腔光固化复合树脂。
Methods: There were 60 cases which included nickel-chromium alloy and porcelain specimens, freshly extracted incisors and porcelain-fused-metal crowns. All were divided into 6 groups with 10 in each group. They are two groups of Ni-Cr alloy or porcelain specimens, one group of incisors and the other of crowns. Each specimen's surface of Ni-Cr alloy and porcelain was bonded with composite resin named Durafill vs by ClearfilSE BONDor Lute according to the guidebook.

4. 摘要] 目的:分析烤瓷用镍铬合金在上瓷前经过阳极钝化,除气预氧化处理后对其表面氧化膜的形貌、厚度的影响。
The sample's metal surface expanded and the thickness of oxide film is 1.72 times of the control samples.

5. 目的 评价IPS Empress 2全瓷冠修复技术修复上颌前牙的临床效果。方法将56例患者172颗牙分成两组,试验组30例86颗牙,以IPS Empress 2全瓷冠修复技术修复;对照组26例86颗牙,以镍铬合金烤瓷冠修复。
Methods A total of 56 patients (172 teeth) were randomly divided into two groups: in the experimental group, 30 patients of 86 teeth were restored with IPS Empress 2 all porcelain crown restoration; and in the control group, 26 patients of 86 teeth were restored with nichrome baked ceramic crown.

6. 镍铬烤瓷的近义词

6. 金沉积烤瓷冠与贵金属合金烤瓷冠的边缘适合性优于镍铬合金烤瓷冠。
The adaptation of precious alloy crown and galvanized forming crown are superior toNi-Cr crown.

7. 目的 对镍铬合金烤瓷冠、贵金属合金烤瓷冠和金沉积烤瓷冠的边缘适合性进行研究,为临床应用提供一定的理论依据和指导。
Objective To compare the adaptation of porcelain fused-to-metal restorations made from Ni-Cr alloy, precious alloy and galvanized forming copings after cementation and to provide a theory guidance for their ap-plication.

8. 分别制作镍铬合金烤瓷冠、贵金属合金烤瓷冠和金沉积烤瓷冠各8个,将3种烤瓷冠在无水酒精中超声清洁5 min,用聚羧酸锌黏固剂按编号将全冠黏固于各自的塑料代型上,指压就位维持10 min。
Methods Three kinds of crowns(Ni-Cr alloy, precious alloy and galvanized forming) were manufactured and cleaned by ultrasonic vibrate with alcoholic solution for 5 minutes, and cemented on their dies as their order. All the crowns were cemented by polycarboxylate zinc-cement and maintained 10 minutes.

9. 镍铬烤瓷

9. 应用正置式反射金相显微镜对经过表面抛光后的镍铬烤瓷合金原始合金和反复熔铸后铸成的各代试样的金相显微结构进行观察;应用X射线粉末衍射仪对镍铬烤瓷合金原始合金和反复熔铸后铸成的各代试样进行物相分析。
The microstructure and the phase structure of original alloy and each generation castings which had been polished by buffing machine were observed and analyzed by metallographic microscope and X-ray diffractometer.

10. 镍铬烤瓷的反义词

10. 本实验为新型烤瓷镍铬合金的研究之一,通过棒盘试验对新型烤瓷镍铬合金、VB钢、CWPA合金进行了比较实验,结果表明新型烤瓷镍铬合金的金瓷结合强度达到或超过目前常用的烤瓷镍铬合金,值得对其进行深入研究。
This laboratory study was to measure the bond strength of a new NiCr alloy to porcelain with pullthrough test, compared to that of the conventional NiCr alloys to porcelain. The results revealed that the bond strength of the new NiCr alloy to porcelain was equal or superior to that of the conventional NiCr alloys to porcelain.

11. 目的:分析反复熔铸对镍铬烤瓷合金化学成分、微观组织结构变化的影响。
OBJECTIVE: To investigate the effects of recasting on the composition and microstructure of Ni-Cr ceramic alloys.

12. 在真空加压氩气保护的铸造环境下,镍铬烤瓷合金各主要元素组分的质量百分数和物相结构随着反复熔铸次数的增多没有发生显著变化,随着熔铸次数的增多其枝晶粗化,合金内部夹杂物和铸造缺陷增多。
There is no significant difference of main composition and phase structure between original alloy and each generation castings in argon protection.

13. 目的:考察新型不含铍的镍铬铝钛烤瓷合金可铸造性能,为新型烤瓷合金的研制和临床应用提供实验依据。
Objective: To study the physical castability of a new type nickel based ceramic alloy w ithout beryllium by comparing with CW-PA alloy and VB alloy, for the purpose of future clinical application.

14. 镍铬烤瓷

14. 纯钛烤瓷冠切缘抗折力902N,镍铬合金烤瓷冠切缘抗折力1029N。
The mean fracture force of Ni-Cr alloy and Titanium is 1029 N and 902 N.

15. 其中镍铬烤瓷合金在真空加氩气保护的环境下反复铸造后金瓷结合力的变化报道较少。
OBJECTIVE: To investigate the effect of recasting on bonding strength of porcelain fused to a Ni-Cr ceramic alloy.

16. 镍铬合金烤瓷冠:内冠是由贱金属镍铬合金铸造而成,在复杂的口腔环境中,暴露在口腔中的金属部分会慢慢分解,并释放黑色的氧化物,导致局部组织染色,这也就是该种修复体会导致牙龈黑线的最重要原因。
1Nie chrome the metal alloy roast a porcelain hat:Inside hat from the base metals Nie chrome metal alloy cast and become, in the complicated mouth cavity environment, the revelation will slowly resolve in the metal part in the mouth cavity, and release black oxide, cause partial organization dyeing, this is also should kind the repair realize the most important reason of causing the gum black line.

17. 目的 在体外模拟环境下,研究溶胶凝胶法制备的涂层对牙科烤瓷镍铬合金耐腐蚀性能的影响。
Methods The bond strength of coating-substrate interface sintered at different temperatures(300, 400, 500, 600 ℃) was tested by scratching method.

18. 金沉积基底冠熔结镍铬桥体烤瓷桥修复3年的临床观察
A three-year clinical evaluation of galvano-ceramic bridges made by Ni-Cr pontic bonding galvano caps

19. 目的:观察金沉积基底冠熔结镍铬桥体烤瓷桥的临床修复效果,为临床利用金沉积技术制作烤瓷桥修复提供参考。
Objective: To evaluate the clinical effect of galvano-ceramic bridges made by Ni-Cr pontic fired bonding galvano caps with highly temperature-resistant adhesive based on three-year clinical trials.

20. 镍铬烤瓷的近义词

20. 镍铬合金镀金烤瓷修复体对牙龈组织健康状况的影响
Effect of Gilt Ni-Cr Alloy PFM on the Gingival Tissue